[求助] 用dynaform做热冲压成形求解时出现的一些问题

    [复制链接]
canquedelanLv.2 显示全部楼层 发表于 2011-11-12 09:42 |阅读模式 打印 上一主题 下一主题
求解器
^_^:
以下是我用dynaform做热成形时出现的一些问题,希望有经验的大神多多指教
1.首先出现关于主从面定义方向问题,计算时出现
** Warning in definition of contact     1
            Master surface offset used in forming contact.
            For this to work properly in thermal contact
            the master surface normals MUST point in the
            direction towards the slave surface.
            Please check your model.

** Warning in definition of contact     2
            Master surface offset used in forming contact.
            For this to work properly in thermal contact
            the master surface normals MUST point in the
            direction towards the slave surface.
            Please check your model.

** Warning in definition of contact     3
            Master surface offset used in forming contact.
            For this to work properly in thermal contact
            the master surface normals MUST point in the
            direction towards the slave surface.
            Please check your model.
我想请教大神们,我在定义的时候都定义了从面法向指向主面啊,这是什么问题呢,这个warning出现了很多次。
2.再就是算法不收敛的问题了,想请教一下,有没有用MAT106材料做过模拟的,指教一下呗
** Warning plasticity algorithm did not converge for MAT106
3.呃,最后就是求解时间步设置的不对了
** Error - the minimum time step has been reached and
             the maximum temperature change is greater than specified
希望有经验的大神对热冲压方面进行一些指导   多谢了

精彩评论3

kofkillerLv.8 显示全部楼层 发表于 2011-11-14 09:31
DYNA没用过热成型,帮顶了。。
canquedelanLv.2 显示全部楼层 发表于 2011-12-20 11:43
问题算是初步解决了,mat106材料模型不收敛是求解设置问题,相关参数也有一定关系,时间步长改小了一点就能算了,这个问题还在研究中,总之是能算出结果来,有兴趣的可以讨论一下
HITZLv.2 显示全部楼层 发表于 2024-9-17 15:37
我先在也是再用这个模型进行热成形,时间步长你是怎么改小的?